Flexible Ti3C2Tx/(Aramid Nanofiber/PVA) Composite Films for Superior Electromagnetic Interference Shielding

Multifunctional electromagnetic interference (EMI) shielding materials would solve electromagnetic radiation and pollution problems from electronic devices. Herein, the directional freeze-drying technology is utilized to prepare the aramid nanofiber/polyvinyl alcohol aerogel with a directionally porous structure (D-ANF/PVA), and the Ti3C2Tx dispersion is fully immersed into the D-ANF/PVA aerogel via ultrasonication and vacuum-assisted impregnation. Ti3C2Tx/(ANF/PVA) EMI shielding composite films with directionally ordered structure (D-Ti3C2Tx/(ANF/PVA)) are then prepared by freeze-drying and hot pressing. Constructing a directionally porous structure enables the highly conductive Ti3C2Tx nanosheets to be wrapped on the directionally porous D-ANF/PVA framework in order arrangement and overlapped with each other. And the hot pressing process effectively reduces the layer spacing between the stacked wavy D-ANF/PVA, to form a large number of Ti3C2Tx-Ti3C2Tx continuous conductive paths, which significantly improves the conductivity of the D-Ti3C2Tx/(ANF/PVA) EMI shielding composite film. When the amount of Ti3C2Tx is 80 wt%, the EMI shielding effectiveness (EMI SE) and specific SE (SSE/t) of D-Ti3C2Tx/(ANF/PVA) EMI shielding composite film achieve 70 dB and 13790 dB·cm2·g−1 (thickness and density of 120 μm and 0.423 g·cm−3), far superior to random-structured Ti3C2Tx/(ANF/PVA) (R-Ti3C2Tx/(ANF/PVA)) composite film (46 dB and 9062 dB·cm2·g−1, respectively) via blending-freeze-drying followed by hot pressing technology. Meanwhile, the D-Ti3C2Tx/(ANF/PVA) EMI shielding composite film possesses excellent flexibility and foldability.


Introduction
With the rapid development and widespread use of flexible wearable electronic equipment and 5G communication technology, the resulting electromagnetic radiation and electromagnetic pollution are increasing [1], which not only interferes with the normal operation of sophisticated electronic devices but also threatens the health of surrounding people [2][3][4]. In recent years, the rapid development of electromagnetic interference (EMI) shielding materials has made the disadvantages of traditional metal materials increasingly apparent [5][6][7]. An urgent need has been raised for materials to be ultrathin and flexible and to have excellent EMI shielding effectiveness (EMI SE), mechanical properties, and corrosion resistance [8][9][10]. Therefore, multifunctional polymerbased EMI shielding composite films have become one of the current research hotspots in the field of EMI shielding materials [11][12][13].
Two-dimensional transition metal carbide/nitride Ti 3 C 2 T x is widely used in the field of EMI shielding due to its excellent conductivity [14][15][16]. Moreover, it has abundant surface functional groups, excellent water dispersibility, and film-forming performance and can be used to prepare polymer-based EMI shielding composite films with excellent comprehensive properties [17][18][19]. At present, most researchers have used blending or layer-by-layer alternating methods to prepare Ti 3 C 2 T x /polymer EMI shielding composite films [20][21][22][23]. When preparing Ti 3 C 2 T x /polymer EMI shielding composite films by blending, highly conductive Ti 3 C 2 T x is disorderly distributed in the insulating polymer matrix [24][25][26]. Usually, a large amount of Ti 3 C 2 T x is required to build the continuous and efficient conductive network, which will affect the processing behaviors and mechanical properties of the composite films [27]. The layer-by-layer alternating method is to arrange the polymer matrix and the highly conductive Ti 3 C 2 T x alternately to prepare Ti 3 C 2 T x /polymer EMI shielding composite films.
The mechanical framing effect exerted by the polymer layer can prevent the nanoscale "sawtooth" cracks in the Ti 3 C 2 T x layer from growing to the entire composite films, giving excellent mechanical properties [28]. However, the multilayer structure destroys the Ti 3 C 2 T x conductive network to a certain extent, causing the electrical conductivity (σ) and EMI SE of the composite films to decrease. The above two general preparation methods both have the problem of disordered conductive networks. It is urgent to explore EMI shielding composite films with an ordered conductive network to improve their σ [29] and at the same time to enhance internal multiple reflections, in order to achieve efficient improvement of EMI shielding performance with a low amount of Constructing an orderly conductive network of the EMI shielding composite films can rely on the preparation of the orderly porous structure aerogel in the early stage [30]. Directional freeze-drying is a novel technology that uses the directional growth of ice crystals to construct directionally porous structures [31][32][33]. It has the characteristics of simple and easy operation, no chemical reaction, and no by-products. Studies have shown that the obtained aerogel with a regularly directionally porous structure can form multiple reflection losses on electromagnetic waves and help to achieve excellent EMI shielding performances [34,35]. Zhao et al. [36] prepared Ti 3 C 2 T x /reduced graphene oxide (Ti 3 C 2 T x /rGO) hybrid aerogels with a directionally porous structure using hydrothermal-assisted self-assembly and directional freeze-drying. When the thickness was 2 mm and the amount of Ti 3 C 2 T x was 0.74 vol%, the EMI SE of the Ti 3 C 2 T x /rGO hybrid aerogel at the X band was as high as 56 dB. Wu et al. [37] prepared Ti 3 C 2 T x /SA aerogel by blending Ti 3 C 2 T x and sodium alginate (SA) via directional freeze-drying and then coated a thin layer of polydimethylsiloxane (PDMS) on the surface of Ti 3 C 2 T x /SA aerogel by dip coating, improving the stability and durability of the porous structure. When the amount of Ti 3 C 2 T x was 95 wt%, the successful construction of the 3D conductive network endowed Ti 3 C 2 T x /SA aerogels excellent σ (2211 S/m) and EMI SE (70.5 dB). However, when simple blendingdirectional freeze-drying is used to prepare aerogels, the highly conductive Ti 3 C 2 T x is mixed with the insulating polymer matrix disorderly. It is still difficult to build a continuous and efficient conductive network and hard to achieve excellent EMI shielding performances with a low amount of Ti 3 C 2 T x [38].
High EMI shielding performances of polymer-based composites with a low amount of Ti 3 C 2 T x can be viable if a polymer framework with a directionally porous structure is prepared by directional freeze-drying, followed by the vacuum-assisted impregnation process to wrap the highly conductive Ti 3 C 2 T x onto the polymer framework [39]. Polyvinyl alcohol (PVA) is an ideal polymer matrix that can be used for directional freeze-drying, but the mechanical properties of PVA aerogels are relatively poor, so that it is difficult to ensure structural stability during ultrasonication and vacuum-assisted impregnation [40,41]. Aramid nanofibers (ANFs) are organic nanofibers with excellent characteristics such as lightweight, high strength, and high temperature resistance [42]. Incorporating high-performance ANFs into PVA is expected to significantly enhance the mechanical properties of PVA aerogels. In addition, the presence of a large amount of air in the pores of the aerogel with a directionally porous structure will make it difficult for Ti 3 C 2 T x wrapped on the polymer framework to contact each other and difficult to form the efficient Ti 3 C 2 T x conductive network, which would exhibit low conductivity. If the aerogels are pressed into films by hot pressing, the layer spacing between the stacked wavy polymer framework can be greatly reduced, facilitating the Ti 3 C 2 T x wrapped on the polymer framework to contact each other. Then, a large number of efficient Ti 3 C 2 T x conductive paths are expected to be formed to significantly improve σ and EMI SE of the composite films.
Herein, directional freeze-drying is used to prepare ANF/PVA aerogels with a directionally porous structure (D-ANF/PVA), and then, Ti 3 C 2 T x dispersion is fully and uniformly immersed into D-ANF/PVA aerogels via ultrasonication and vacuum-assisted impregnation. Ti 3 C 2 T x /(ANF/ PVA) aerogels with a directionally porous structure (D-Ti 3 C 2 T x /(ANF/PVA)) are obtained by freeze-drying, and then, the directionally ordered D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films are prepared by hot pressing. The effects of the amount of Ti 3 C 2 T x on σ, EMI SE, and mechanical properties of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films are discussed in detail.

Results and Discussion
The process of preparing D-Ti 3 C 2 T x /(ANF/PVA) and R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films is shown in Figure 1. The directional freeze-drying technology is utilized to prepare the D-ANF/PVA aerogel, and the Ti 3 C 2 T x dispersion is fully and uniformly immersed into the D-ANF/PVA aerogel via ultrasonication and vacuumassisted impregnation. The D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films with a directionally ordered structure are prepared by freeze-drying and hot pressing. The R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films are prepared by blending-freeze drying-hot pressing technology. The experimental details can be found in Materials and Methods.
From Figures 2(a) and 2(b), the ANF fibers are slender threads, with length of about 5~10 μm and diameter of about 40~50 nm, and they overlap each other. This is attributed to the fact that there are amide bonds between the molecular chains of Kevlar fibers, and strong hydrogen bonds are formed between the molecular chains. After being treated with strong base KOH, the hydrogen in the amide group undergoes deprotonation; a large number of hydrogen bonds are destroyed and gradually dissociated [43]. The electrostatic repulsion between the molecular chains further promotes the dissociation of the Kevlar fiber and gradually reduces the Kevlar fiber size. However, the entanglement of the molecular chains causes the benzene rings to stack on each other to generate π-π conjugated interaction force, which prevents the Kevlar fiber from disintegrating completely, thus forming nanofibrous ANFs. , and (006) crystal planes, respectively, mainly due to the regular arrangement of the molecular chain structure inside the Kevlar fiber and the abundant hydrogen bond interactions that give rise to a higher degree of crystallinity [44]. The intensity of the crystallization peak in ANFs is greatly reduced, only with a broad diffraction peak near 20°, indicating that the crystal structure of Kevlar fiber is dissociated and the hydrogen bond between molecular chains is broken [45]. Ti 3 AlC 2 has a compact layered structure ( Figure 2(d)) [46]. After etching with hydrofluoric acid generated in situ by lithium fluoride and hydrochloric acid, Ti 3 C 2 T x nanosheets with a twodimensional lamella structure are obtained ( Figure 2(e)). Ti 3 C 2 T x nanosheets are highly transparent under electron irradiation ( Figure 2(f)), indicating that they are very thin and have a clear surface without impurities [47]. The corresponding selected area electron diffraction (SAED) (Figure 2(g)) shows that the Ti 3 C 2 T x nanosheets have a typical hexagonal crystal structure. From the AFM image ( Figure 2(h)), the Ti 3 C 2 T x nanosheets are regular in shape, with radial size of about 1.4 μm and thickness of about 2 nm. The XRD spectrum of Ti 3 C 2 T x nanosheets ( Figure 2(i)) shows sharp diffraction peaks at 6°and weaker diffraction peaks at 13°, 19°, 26°, and 32°, corresponding to (002), (004), (006), (008), and (010) crystal planes, respec-tively [48,49]. The peak at 39°for the (104) crystal plane in Ti 3 AlC 2 disappears, and the peak intensity of the (002) crystal plane is much higher than others [50,51]. The above characterizations indicate the successful preparation of fewlayered Ti 3 C 2 T x . Figure 3(a) shows σ of R-Ti 3 C 2 T x /(ANF/PVA) and D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films. With the increase in the amount of Ti 3 C 2 T x , σ of R-Ti 3 C 2 T x /(ANF/PVA) and D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films show the trend of rapid increase. This is because the intrinsic conductivity of Ti 3 C 2 T x is very high. With the increase in the amount of Ti 3 C 2 T x , the conductive networks inside the composite films are gradually improved to be complete, leading the conductivity of the composite films to increase with the increase in the amount of Ti 3 C 2 T x [52,53]. When the amount of Ti 3 C 2 T x is 80 wt%, σ of the R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film increases to 188.7 S/m, and that of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film is as high as 357.1 S/m, much higher than that of the R-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film. This is because Ti 3 C 2 T x is disorderly distributed in the R-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film, and ANFs and PVA are interspersed between the conductive Ti 3 C 2 T x layers, making it difficult to form an efficient conductive network (Figures 4(a) and 4(b") and Figure S2 Ice crystals 3 Research PVA aerogel prepared by directional freeze-drying has a neat and directionally porous structure (Figures 4(c)-4(c")). In the directional freezing process, the water in the ANF/PVA dispersion is affected by the supercooling provided by the cold source to form ice crystals, which grow vertically upwards along the freezing gradient direction, promoting the orderly arrangement of ANF/ PVA along the growth direction of the ice crystals. During the low-pressure drying process, the ice crystals sublime to obtain D-ANF/PVA aerogel with a directionally porous structure. After pouring the Ti 3 C 2 T x dispersion, highly conductive Ti 3 C 2 T x nanosheets are neatly and orderly wrapped onto the outer surfaces of the D-ANF/PVA aerogel and the inner walls of the through-hole, forming a directionally ordered continuous 3D conductive network ( Figure S1(a-a")). Furthermore, the hot pressing process compresses the directional hole wall between the D-Ti 3 C 2 T x /(ANF/PVA) aerogel (Figures 4(d)-4(d") and Figure S2(b)), and the Ti 3 C 2 T x nanosheets in the throughhole are in efficient contact. The D-ANF/PVA aerogel contains C element, while D-Ti 3 C 2 T x /(ANF/PVA) aerogel and corresponding composite film contain not only C element but also Ti element. This is mainly due to the successful introduction of Ti 3 C 2 T x . Therefore, a large number of continuous and efficient Ti 3 C 2 T x conductive paths are formed, and σ of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films is significantly improved [54]. As shown in Figures 3 Figures S3 and S4 show the total shielding effectiveness (SE T ), absorption shielding effectiveness (SE A ), and reflection shielding effectiveness (SE R ) of R-Ti 3 C 2 T x /(ANF/PVA) and D-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite films at the X band, respectively. The SE T , SE A , and SE R of ANF/PVA composite films are all very low, about 0.4 dB, 0.3 dB, and 0.1 dB, respectively. As the amount of Ti 3 C 2 T x increases, the SE T , SE A , and SE R of R-Ti 3 C 2 T x /(ANF/PVA) and D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films increase significantly. When the amount of Ti 3 C 2 T x is 80 wt%, the SE T , SE A , and SE R of the D-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film reach 70 dB, 24 dB, and 46 dB, respectively, much higher than SE T (46 dB), SE A (16 dB), and SE R (30 dB) of the R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film ( Figure 5(c)). Meanwhile, D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film has higher EMI shielding efficiency. When the amount of Ti 3 C 2 T x is 80 wt%, D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film is capable of blocking 99.99999% of electromagnetic wave radiation, far better than that of R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film, which could block 99.997% of electromagnetic wave radiation ( Figure 5(d)).
Poor EMI shielding performance of the R-Ti 3 C 2 T x /(ANF/PVA) composite films is mainly attributed to the disorderly arrangement of the Ti 3 C 2 T x nanosheets inside. Contact between Ti 3 C 2 T x as well as formation of an effective Ti 3 C 2 T x conductive network is difficult, making σ low. In addition, the disorderly and chaotic arrangement of

Research
Ti 3 C 2 T x nanosheets in the R-Ti 3 C 2 T x /(ANF/PVA) composite film also results in less internal multiple reflection and scattering of electromagnetic waves.
As shown in Figure S5, we performed 500 and 1000 folding cycles of the D-Ti 3 C 2 T x /(ANF/PVA) composite film with the mass fraction of Ti 3 C 2 T x of 80 wt%. It can be seen that its EMI shielding effectiveness has almost no change, which shows that the EMI shielding performance of composite film is stable and repeatable.
Superior EMI shielding performance of D-Ti 3 C 2 T x /(ANF/PVA) composite films is mainly due to its multiple EMI shielding effects. Firstly, the construction of a directionally ordered structure and the adoption of the hot pressing process give the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films higher σ, which is more different from the σ of air, causing greater impedance mismatch. Therefore, when external electromagnetic waves are incident on the surface of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films, a large proportion of them is immediately reflected back into the air [55]. Secondly, due to the excellent σ of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films, microcurrents are generated by electromagnetic waves through charge carriers, which enhances the ohmic loss of electromagnetic waves and reduces the energy of electromagnetic waves [56]. Thirdly, a large amount of internal multiple reflection and scattering for remaining electromagnetic waves occur between the neatly arranged and parallel Ti 3 C 2 T x layers, where the energy of electromagnetic waves is converted into heat in the form of microcurrent, thus greatly enhancing the loss of electromagnetic wave energy [57], further improving the electromagnetic wave absorption ability of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding com-posite films. Lastly, the electromagnetic waves also experience polarization loss with the functional groups (-OH, -F, etc.) on the surface of Ti 3 C 2 T x [58]. Therefore, D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films have higher EMI SE than that of R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films. Therefore, the neat and orderly D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films realize the reflection of electromagnetic waves, internal multiple reflections, and absorption loss, and only a very small amount of electromagnetic waves could pass through the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films, which can greatly reduce the electromagnetic pollution to the environment as well as the harm to human health ( Figure 5(g)).
In order to further prove the superiority of the EMI shielding performance of the D-Ti 3 C 2 T x /(ANF/PVA) composite films, the obtained EMI shielding performances in this work have been compared with other polymer-based materials reported in literatures (Tables S2 and S3). 6 Research and 6(e). The tensile properties of the D-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film stretched parallel to the directional freezing direction is much higher than that of the R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film. When the amount of Ti 3 C 2 T x is 80 wt%, the tensile strength and elongation at break of the R-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film are 8.4 MPa and 2.7%, respectively. At the same amount of Ti 3 C 2 T x , the tensile strength and elongation at break of the D-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film stretched parallel to the directional freezing direction are 13.1 MPa and 4.2%, respectively. This is because the distribution of Ti 3 C 2 T x in the R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film is relatively chaotic and disorderly, and more stress concentration points are easily generated when subjected to external forces. For D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films, the structure is directionally ordered parallel to the directional freezing direction, and its stress distribution is uniform, giving it high tensile strength and elongation at break [59,60]. In addition, when the amount of Ti 3 C 2 T x is 80 wt%, the tensile strength and elongation at break of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film stretched perpendicular to the directional freezing direction are 6.1 MPa and 1.7%, respectively, lower than 7 Research those of D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film stretched parallel to the directional freezing direction, indicating that the mechanical properties of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films are anisotropic. This may be attributed to the fact that the structural strength perpendicular to the directional freezing direction is relatively weak, and the weaker intermittent connection will break under lower tensile strength. In contrast, the structure parallel to the directional freezing direction is relatively complete, with fewer internal defects [61,62]. Moreover, it should be noted that the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film can be folded into a paper boat and bent into circle, "S," and heart shapes ( Figure 6(e)), indicating that it has excellent flexibility and foldability.

Conclusions
Construction of the directionally porous structure enables the highly conductive Ti 3 C 2 T x nanosheets to be wrapped on the directionally ordered D-ANF/PVA framework in orderly arrangement and overlapped with each other, achieving a more efficient and complete conductive network with the same amount of Ti 3 C 2 T x . The hot pressing would process greatly reduce the layer spacing between the stacked wavy D-ANF/PVA and enable a large number of Ti 3 C 2 T x nanosheets wrapped on the D-ANF/PVA framework to efficiently contact. A large number of Ti 3 C 2 T x -Ti 3 C 2 T x continuous conductive paths are formed, which significantly improve σ of D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films. When the amount of Ti 3 C 2 T x is 80 wt%, EMI SE and SSE/t of D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film achieve 70 dB and 13790 dB·cm 2 ·g -1 (thickness and density of 120 μm and 0.423 g·cm -3 ), far superior to R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film (46 dB and 9062 dB·cm 2 ·g -1 , respectively) prepared by blending-freeze drying followed by hot pressing technology. The mechanical properties of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films are anisotropic. When the amount of Ti 3 C 2 T x is 80 wt%, the tensile strength and elongation at break stretched parallel to the directional freezing

Materials and Methods
4.1. Preparation of D-ANF/PVA Aerogels. A certain amount of ANFs and PVA were added into 30 mL of deionized water, to obtain the ANF/PVA dispersion by ultrasonication. Then, the above mixtures were poured into a homemade mold (copper at the bottom and polytetrafluoroethylene around), followed by being placed into the liquid nitrogen to freeze. Then, the frozen products were placed in the vacuum freeze dryer for 72 hrs to obtain the D-ANF/PVA aerogels with directionally porous structures.

4.2.
Fabrication of D-Ti 3 C 2 T x /(ANF/PVA) and R-Ti 3 C 2 T x /(ANF/PVA) EMI Shielding Composite Films. A certain amount of Ti 3 C 2 T x (prepared based on the minimally intensive layer delamination (MILD) method in accordance with our previous works [63]) was dispersed in deionized water to obtain Ti 3 C 2 T x aqueous dispersion. Subsequently, the obtained D-ANF/PVA aerogels were immersed in the Ti 3 C 2 T x dispersion, and the Ti 3 C 2 T x aqueous dispersion was fully filled into the ANF/PVA aerogels via ultrasonication and vacuum-assisted impregnation process. Then, the ANF/PVA aerogels impregnated with Ti 3 C 2 T x aqueous dispersion were placed in liquid nitrogen and were then placed in the vacuum freeze dryer for 72 hrs to obtain D-Ti 3 C 2 T x /(ANF/PVA) aerogels. In this work, D-Ti 3 C 2 T x /(ANF/ PVA) aerogels with Ti 3 C 2 T x amount of 20 wt%, 40 wt%, 60 wt%, and 80 wt% were prepared, respectively. Finally, the D-Ti 3 C 2 T x /(ANF/PVA) aerogels were hot pressed at 50°C and 20 MPa for 10 min to obtain D-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite films. For comparison, random-structured Ti 3 C 2 T x /(ANF/ PVA) (R-Ti 3 C 2 T x /(ANF/PVA)) EMI shielding composite films were also prepared. A certain amount of Ti 3 C 2 T x , ANFs, and PVA were dispersed in deionized water, mixed uniformly by ultrasonication to obtain Ti 3 C 2 T x /(ANF/ PVA) solution. Subsequently, the beaker containing Ti 3 C 2 T x /(ANF/PVA) solution was placed in liquid nitrogen, followed by staying in the vacuum freeze dryer for 72 hrs to obtain R-Ti 3 C 2 T x /(ANF/PVA) aerogels. Finally, the R-Ti 3 C 2 T x /(ANF/PVA) aerogels were hot pressed at 50°C and 20 MPa for 10 min to obtain R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite films.
Specific experimental details such as raw materials and characterizations are provided in Supplementary Materials.

Data Availability
The data in this paper cannot be shared at this time as the data also forms part of an ongoing study.

Additional Points
Highlights. 1. Directionally porous structure is constructed so that the highly conductive Ti 3 C 2 T x nanosheets are wrapped on the directionally ordered D-ANF/PVA framework in order arrangement and overlapped each other. 2. Hot-press process effectively reduces the layer spacing between the stacked wavy D-ANF/PVA, to form a large number of Ti 3 C 2 T x -Ti 3 C 2 T x continuous conductive paths, which significantly improves the conductivity of the D-Ti 3 C 2 T x / (ANF/PVA) EMI shielding composite film. 3. When the amount of Ti 3 C 2 T x is 80 wt%, the EMI SE and SSE/t of D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film achieve 70 dB and 13790 dB·cm 2 ·g -1 (thickness and density of 120 μm and 0.423 g·cm -3 ), far superior to R-Ti 3 C 2 T x /(ANF/ PVA) EMI shielding composite film (46 dB and 9062 dB·cm 2 ·g -1 , respectively) by blending-freeze drying followed by hot pressing technology. 4. Mechanical properties of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film are anisotropic. When the amount of Ti 3 C 2 T x is 80 wt%, the tensile strength of the D-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film stretched parallel to the directional freezing direction are 13.1 MPa, significantly better than the tensile strength (8.4 MPa) of the R-Ti 3 C 2 T x /(ANF/PVA) EMI shielding composite film.